GEMSTONE

SHT – WHITE

Super high translucent zirconia

Disc system:

Translucency: 48%

Strength: 1250MPa

Sizes : 10mm/12mm/14mm/16mm/18mm/20mm/22mm/25mm/30mm

Shades: White

PARAMETER
Physical Characteristics
Density after sintering ≥6.08g/cm3
Fracture Toughness ≥5.0Mpa.m1/2
Flexural strength after sintering (Hv10) 1250
Sintering Temperature 1530℃
Chemical Compositions
ZrO2 + HfO2 + Y2O3 ≥99%
Y2O3 7.0%-7.8%
Al2O3 <0.15%
Other Oxides <0.15%
DISPLAY
Shading Liquids

Immersion Shading Liquids:

  • Rich natural shades
  • Pair with VITA shades
  • Meet diverse esthetics needs

16 VITA Classical Shades

Suitable for denture zirconia blockesthetics material

Volume:50ml
Shades: A1, A2, A3, A3.5, A4, B1, B2, B3, B4, C1, C2, C3, C4, D2, D3, D4

26 VITA Classical Shades

Suitable for denture zirconia blockesthetics material
Volume:50ml
Shades: 1M1, 1M2, 2L1.5, 2L2.5, 2M1, 2M2, 2M3, 2R1.5, 2R2.5, 3L1.5, 3L2.5, 3M1, 3M2, 3M3, 3R1.5,3R2.5, 4L1.5, 4L2.5, 4M1, 4M2, 4M3, 4R1.5, 4R2.5, 5M1, 5M2, 5M3

Diluent

Make the pontic shade lighter of denture zirconia block esthetics materialVolume:50ml

Incisal Effect Liquids

Increase the incisal translucency of ST zirconia block material
Volume:50ml

GEMSTONE

SHT – COLOR

Super high translucent colored zirconia

Disc system:

Translucency: 47%

Strength: 1150MPa

Sizes : 10mm/12mm/14mm/16mm/18mm/20mm/22mm/25mm/30mm

Shades: A1,A2,A3,B1,B2

PARAMETER
Physical Characteristics
Density after sintering ≥6.08g/cm3
Fracture Toughness ≥5.0Mpa.m1/2
Flexural strength after sintering (Hv10) 1250
Sintering Temperature 1530℃
Chemical Compositions
ZrO2 + HfO2 + Y2O3 ≥99%
Y2O3 7.0%-7.8%
Al2O3 <0.15%
Other Oxides <0.5%

Indications

Millable Material

GEMSTONE

SHT – MULTI

Super high translucent multilayer zirconia

Disc system:
Translucency: 47%
Strength: 1150MPa
Sizes : 10mm/12mm/14mm/16mm/18mm/20mm/22mm/25mm/30mm
Shades: A1,A2,A3,B1,B2,BL1,BL2,BL3,BL4

  • Better transparency and better aesthetics.
  • Four layers of material overlay, seven layers of color gradient.
  • The first choice of aesthetic restorative materials for anterior teeth.
PARAMETER
Physical Characteristics
Density after sintering ≥6.08g/cm3
Fracture Toughness ≥5.0Mpa.m1/2
Flexural strength after sintering (Hv10) 1250
Sintering Temperature 1530℃
Chemical Compositions
ZrO2 + HfO2 + Y2O3 ≥99%
Y2O3 7.0%-7.8%
Al2O3 <0.15%
Other Oxides <0.5%

Indications

Millable Material
DISPLAY

Brochure, Accessories Price List, Instructions & other files

GO TO DOWNLOAD CENTER
Thank you for your message. It has been sent.
There was an error trying to send your message. Please try again later.